I-WD1000 / 1100 Wear Plate

Ipuleti evamile yokugqoka i-chromium carbide, efanelekile ukusetshenziswa kuzinhlelo zokusebenza zokugqoka ezibandakanya umthelela ophansi ukuya kokuphakathi.
Usayizi weshidi: 1400 * 3400mm, 1500 * 3000mm, abanye ngesicelo
Ukuqina: 58-65HRC


Imininingwane yomkhiqizo

production introduction

WD1000 / WD1100 uchungechunge
I-Abrasion Resistant Chromium Carbide Imbondela

logo

I-WD1000 / WD1100 iyi-chromium carbide composite cladding fusion eboshelwe kupuleti lensimbi elincane elisekelayo. Idiphozi itholakale ngokusebenzisa i-flux cored arc welding. Ipuleti lokugqoka le-WD1000 / WD1100 lilungele ukufaka isicelo okubandakanya ukuhuzuka okuphezulu nomthelela ophansi ukuya kokuphakathi.

Uchungechunge lwe-WD1000 / WD1100:

Amapuleti ajwayelekile wokugqoka i-chromium carbide akhiqizwa yi-flux cored arc welding; Ifanele izinhlelo zokusebenza ezibandakanya ukuhuzuka okuphezulu nomthelela ophansi ukuya kokuphakathi.

Amakhemikhali

Ubulukhuni

Usayizi Weshidi

I-Base Metal

C - Cr - Fe

HRC 58-63

1400 * 3400

Q235 / Q345. njll

Ukwakhiwa Kwamakhemikhali (%)

C

Cr

Mnu

Si

Fe

Okunye

3.0-5.0

15.0-35.0

1.0-3.0

1.0-3.0

Bal.

-

Ubulukhuni

HRC 58-65

Ubukhulu obujwayelekile (mm)

3 + 3; 4 + 4; 5 + 5; 6 + 4; 6 + 6; 8 + 4; 8 + 6; 8 + 8; 10 + 10; 12 + 12; njll

(imbondela ukushuba kuze kufike ku-50mm)

Usayizi Weshidi Ojwayelekile (mm)

1400 * 3400; 1500 * 3000; 2000 * 3000;

(Usayizi owenziwe ngokwezifiso uyatholakala)

Inqubo ye-ASTM G65 A

0.12 - 0.18g

Ithempelesha yokusebenza

<400 ℃

I-Base Metal Material

Q235B, Q345B; A36; I-S235JR nezinsimbi zokwakha

Imboni Eyinhloko

Izimayini, imboni yengilazi, isamente, isitshalo sensimbi, isitshalo samandla, njll

Ubuqili

Plasma ahlabayo, Gouging, Countersunk, stud umshudo, Bending

 

Singakwazi ukwenza ngokwezifiso amapuleti ngosayizi ohlukile nokushuba ngokususelwa kwimidwebo yekhasimende. singakwazi futhi ukusika, ukugoba kanye nokushisela amapuleti okuguga kubunjwa nezingxenye ezithile

Izici:

  • * I-Chromium carbide imbondela gqoka ipuleti elingazweli
    * Ukwakhiwa kwamakhemikhali: C: 3.0-5.0% Cr: 18-30%
    * I-Chromium carbide Cr7C3 ivolumu yengxenyana engaba ngu-40%
    * Ubukhulu besendlalelo esimelana nokugqoka bungafinyelela ku-50 mm
    * Ukumelana nokushisa kuze kufike ku-600 ° C
    * Indawo emelana nokugqoka ejwayelekile engu-1400 * 3400mm, 1500 * 3000mm, 2000 * 3000mm
    * Flatness Better nge ebusweni bushelelezi
    * Ubulukhuni: HRC58-65
open arc wear plate
open arc wear plate04
open arc wear plate02
open arc wear plate03

Qaphela:Okuqukethwe kweCarbon neChromium kuyahlukahluka kupuleti elihlukile.